Glass microfiber filters offered in this product range are produced from 100% borosilicate glass microfiber without the use of binders or strengthening agents. These filters offer many advantages in a wide range of analytical applications. The fibers used to manufacture these depth filters are…

These filters are washed three times with deionized water, dried at 105°C, then furnace treated at 550°C to remove any volatile components. They are then weighed to 0.0001g. Each filter is in an individual aluminum pan with the filter weight printed on a Mylar® label affixed to the pan.…

Depth filtration glass micro fiber GRADE A-E - Fine porosity and fast flow rate, with a 1.0 µm size particle retention. Binderless borosilicate glass microfiber. DOP efficiency is 99.98%. Primarily used in suspended solids and air monitoring. Particle retention: 1.00 µm …

Qualitative cellulose filter papers perform separation by entrapping particulate within the random matrix of cellulose fibers within the depth of the media. This media is widely used in methods requiring the determination and identification of particulate in both liquids and gas. Also, this natural…

Depth Filtration Glass Micro Fiber GRADE C - Fine porosity, fast flow rate, with a 1.2 µm size particle retention. Primarily used for RIA procedures and harvesting lymphocytes. Binderless borosilicate glass microfiber. Particle retention: 1.20 µm Filtration speed: 25 seconds Thickness: 0.28…

Ahlstrom offers a full range of standard pleated grades that meet your needs from grades with rapid flow rates for filtration of viscous materials to grades with tight matrices for removal of fine precipitates. Ahlstrom’s pre-pleated grades can save valuable time and maximize the efficiency…

Ahlstrom's qualitative grades of filter paper are, by definition, recommended for use in analytical methods, which determine or identify particulate constituents of a mixture irrespective of the amount present. Qualitative filter papers are often used in routine separation work that still…

Ahlstrom’s qualitative grades of filter paper are, by definition, recommended for use in analytical methods, which determine or identify particulate constituents of a mixture irrespective of the amount present. Qualitative filter papers are often used in routine separation work that still…

ValuSep® 5um Glass Micro Fiber (GMF) prefilters are made of two separate layers of glass fiber in a very thin format for highly efficient capture and retention of particles that could prematurely clog an SPE filter.

I.W. Tremont offers a diverse product line of high quality membrane filters available in a variety of materials, diameters and pore sizes and suitable for a wide range of applications including cell retention, In Vitro Diagnostics, particle collection, clarification and sterile filtration of…

Depth filtration glass micro fiber GRADE E - Fine porosity, fast flow rate, with a 1.3 µm size particle retention. This material is an economical media for suspended particle analysis in water, cell harvesting, pre-filtration and air monitoring applications. Binderless borosilicate…

Ahlstrom manufactures a series of extremely high purity, acid washed filter papers designed for use in analytical and gravimetric analysis. The quantitative grades are manufactured from top quality cotton linters using ultra-pure, reverse-osmosis water and are further treated with dilute acid to…

Depth filtration glass micro fiber GRADE F - Fine porosity, medium flow rate, with a 0.7 µm size particle retention. Frequently used with Grade D to filter diluted aqueous solutions containing strong oxidizing, acidic, or alkaline components prior to laser spectroscopy. May also be used for TCLP…

Suitable for routine gravimetric analysis and typical preparation of samples for use in analysis involving instrumental techniques. Low ash grades have intermediate ash content between qualitative grades and ashless grades. Grade 392 is medium to slowly filtering and used for fast filtration…

Quantitative cellulose filter papers are primarily used in gravimetric analysis procedures and perform separations by entrapping particulate within the random matrix of cellulose fibers within the depth of the media. This media family is also widely used in methods to prepare samples for further…

Designed for general qualitative laboratory work Fast filtering speed; 25um particle retention Low retentivity, which retains coarse or gelatinous precipitates such as aluminum hydroxide, cobalt carbonate, mercury iodide and magnesium hydroxide Creped surface; thickness approximately…

A deep black, qualitative paper for filtering light colored sediments, etc. Medium speed Retains crystalline precipitates of medium fineness 6 µm pore size

Depth filtration glass micro fiber GRADE A - Fine porosity, fast flow rate, with a 1.6µm size particle retention. Frequently used in the filtration of precipitated proteins and cells. Ideally suited for use as a filter for radioimmuno assay of weak beta emitters by scintillation…

ProWeigh® Filters are 1.5µm Binderless Glass Fiber Filters with all preparation steps done for you. All ProWeigh filters are prepared according to Standard Methods requirements. 47mm binderless glass fiber filters are weighed, washed 3 times in deionized water, dried at 105C and…

Depth filtration glass micro fiber GRADE B - Fine porosity, medium to fast flow rate, with a 1.0 µm size particle retention. Ideally suited for the collection of biochemical polymers that have been precipitated by denaturation. This material is twice as thick as Grade A with a higher loading…

Depth filtration glass micro fiber 934-AH® - Fine porosity, fast flow rate, with a 1.5 µm size particle retention. This material is the standard for volatile suspended solids content and related measurements (Standard Methods 2540D and EPA Method 160.2). Also widely used in cell harvesting…

Qualitative wet-strengthened filter paper grades are manufactured for applications using in a system or apparatus that operates under pressure or vacuum conditions. They contain a small amount of chemically stable, insoluble binding resin which strengthens the natural fiber-to-fiber bonds under wet…

Ahlstrom’s qualitative grades of filter paper are, by definition, recommended for use in analytical methods, which determine or identify particulate constituents of a mixture irrespective of the amount present. Qualitative filter papers are often used in routine separation work that still…

Depth Filtration Glass Micro Fiber GRADE D - Coarse porosity, fast flow rate, with a 2.7 µm size particle retention. Well suited for higher volume and repetitive laboratory filtering. Also ideally used as a general pre-filter to extend primary filter life. Binderless borosilicate glass…

Xenomax® Pre-Weighed TSS Filters are pre-washed, predried, pre-desiccated, and pre-weighed in accordance with Standard Methods 2540 D and are ready to use out of the box. To significantly speed up TSS analysis, simply filter your sample, dry the filter, and record its final weight. These…

Advantec Qualitative Filter Papers are made of 100% cotton linter cellulose. Primarily used for clarifying and removing precipitates (ppt) and preparation for quantitative analysis. These papers can be used over a pH range from 0-12 and a maximum temperature of 120°C. Ash content of 0.1%.…

Designed for very fine precipitates Slow filtering speed; 1 µm particle retention High retentivity, which retains very fine crystalline precipitates such as cuprous oxide, lead sulfate, barium sulfate and manganese carbonate Thickness approximately 0.20 mm, 1.5 µm pore size

Ahlstrom’s qualitative grades of filter paper are, by definition, recommended for use in analytical methods, which determine or identify particulate constituents of a mixture irrespective of the amount present. Qualitative filter papers are often used in routine separation work that still requires…

Ahlstrom offers a full range of glass microfiber filters manufactured from 100% pure borosilicate glass. Because of their intrinsic properties, glass microfiber filters have wide applications in many areas of laboratory analysis, especially when fine filtration and high loading capacity is…

Advantec Quantitative Ashless Filter Papers are made from the highest quality alpha cotton cellulose. One critical step in the manufacturing process of these filter papers is acid washing. All grades are double acid washed in hydrochloric then hydrofluoric acid to reduce levels of SiO2, CaO, and…

Binder-free, fast flowing, fine porosity borosilicate glass microfiber filters have been optimized for better wet strength/handleability and high temperature (550°C) blank stability; two quality issues known to affect other brands of TSS filters. Xenomax TSSFVS Filters are readily available in…